Ammonia production catalyst and after treatment system

ABSTRACT

An after treatment system is disclosed. The after treatment system may include an exhaust pipe through which an exhaust gas flows; a three-way catalyst (TWC) mounted on the exhaust pipe and purifying HC, CO, and NOx contained in the exhaust gas, an ammonia production catalyst (APC) mounted on the exhaust pipe at a downstream of the TWC, storing NOx at a lean air/fuel ratio, and generating H 2 , releasing the stored NOx, and generating NH 3  using the released NOx and the generated H 2  at a rich air/fuel ratio, and a selective catalytic reduction (SCR) catalyst mounted on the exhaust pipe at a downstream of the APC, storing the NH 3  generated in the TWC and the APC, and reducing the NOx contained in the exhaust gas using the stored NH 3 .

FIELD

The present disclosure relates to an ammonia production catalyst (APC) and an after treatment system.

BACKGROUND

The statements in this section merely provide background information related to the present disclosure and may not constitute prior art.

Vehicles may be provided with at least one catalytic converter for reducing emission (EM) contained in an exhaust gas. The exhaust gas flowing out from an engine through an exhaust manifold is driven into a catalytic converter mounted at an exhaust pipe and is purified therein. After that, noise of the exhaust gas is decreased while passing through a muffler and then the exhaust gas is emitted into the air through a tail pipe. The catalytic converter purifies the EM contained in the exhaust gas. In addition, a particulate filter for trapping particulate matter (PM) in the exhaust gas is mounted in the exhaust pipe.

A three-way catalyst (TWC) is one type of the catalytic converter and reacts with hydrocarbon (HC) compounds, carbon monoxide (CO) and nitrogen oxides (NOx), which are harmful components of the exhaust gas, to remove these compounds. The TWCs are mainly installed in gasoline vehicles, and Pt/Rh, Pd/Rh or Pt/Pd/Rh systems are used as the TWCs.

A lean-burn engine among gasoline engines may improve fuel efficiency by burning a lean air/fuel mixture. The lean-burn engine burns the lean air/fuel mixture, so air/fuel ratio of the exhaust gas is also lean. However, when the air/fuel ratio is lean, the TWC slips the NOx without reducing all of the NOx contained in the exhaust gas. Accordingly, a vehicle equipped with the lean-burn engine may include a selective catalytic reduction (SCR) catalyst for purifying the NOx slipped from the TWC. The SCR catalyst used in the vehicle equipped with the lean-burn engine may be a passive type SCR catalyst.

When the air/fuel ratio is rich, the TWC reduces the NOx to produce NH3 and the NH3 generated in the TWC is stored in the passive type SCR catalyst. When the air/fuel ratio is lean, the passive type SCR catalyst purifies the NOx contained in the exhaust gas using the stored NH₃.

The lean-burn engine, which includes the TWC and the passive type SCR catalyst, may control the air/fuel ratio to be rich by increasing the fuel amount during a predetermined period to store sufficient NH3 in the passive type SCR catalyst. If the amount of the NOx discharged from the lean-burn engine increases, the number and duration where the lean-burn engine operates at the richer air/fuel ratio also increase. Therefore, fuel economy may be deteriorated.

The above information disclosed in this Background section is only for enhancement of understanding of the background of the disclosure and therefore it may contain information that does not form the prior art that is already known to a person of ordinary skill in the art.

SUMMARY

The present disclosure provides an ammonia production catalyst (APC) having advantages of generating NH₃ at a rich air/fuel ratio.

Another aspect of the present disclosure provides an after treatment system having further advantages of increasing NH₃ supplied into a selective catalytic reduction (SCR) catalyst at the rich air/fuel ratio by disposing the APC between a three-way catalyst (TWC) and the SCR catalyst.

An ammonia production catalyst (APC) according to an form of the present disclosure may include 0.4-0.9 wt % of Pt, 0.057-0.3 wt % of Pd, 0.03-0.1 wt % of Rh, 5.0-15.0 wt % of Ba, 10-30 wt % of CeO₂, 48.7-84.513 wt % of a composite of MgO and Al₂O₃, and 0-5 wt % of an additive based on a total weight of the APC.

The additive may include at least one of La, Zr, Mg, and Pr.

The composite of MgO and Al₂O₃ may include 15-25 wt % of MgO based on a total weight of the composite of MgO and Al₂O₃.

A weight ratio of Pt to Pd may be 3:1 to 7:1.

An ammonia production catalyst (APC) according to another form of the present disclosure may include 0.4-0.9 wt % of Pt, 0.057-0.3 wt % of Pd, 0.03-0.1 wt % of Rh, 5.0-15.0 wt % of Ba, 10-25 wt % of CeO₂, 48.7-79.513 wt % of a composite of MgO and Al₂O₃, and 0-10 wt % of an additive based on a total weight of the APC.

The additive may include at least one of La, Zr, Mg, and Pr.

The composite of MgO and Al₂O₃ may include 15-25 wt % of MgO based on a total weight of the composite of MgO and Al₂O₃.

A weight ratio of Pt to Pd may be 3:1 to 7:1.

An after treatment system according to an form of the present disclosure may include: an exhaust pipe through which an exhaust gas flows; a three-way catalyst (TWC) mounted on the exhaust pipe and purifying HC, CO, and NOx contained in the exhaust gas; an ammonia production catalyst (APC) mounted on the exhaust pipe at a downstream of the TWC, storing NOx at a lean air/fuel ratio, and generating H₂, releasing the stored NOx, and generating NH₃ using the released NOx and the generated H₂ at a rich air/fuel ratio; and a selective catalytic reduction (SCR) catalyst mounted on the exhaust pipe at a downstream of the APC, storing the NH₃ generated in the TWC and the APC, and reducing the NOx contained in the exhaust gas using the stored NH₃.

The after treatment system may further include a CO clean-up catalyst (CUC) mounted on the exhaust pipe at a downstream of the SCR catalyst and purifying the CO contained in the exhaust gas.

The after treatment system may further include a particulate filter disposed between the TWC and the APC or between the APC and the SCR catalyst, wherein the particulate filter traps particulate matter in the exhaust gas.

In one aspect, the APC may include Pt, Pd and CeO2, wherein a weight ratio of Pt to Pd is 3:1 to 7:1, and wherein weight ratio of the CeO2 to a total weight of the APC is 10-30 wt %.

In another aspect, the APC may include 0.4-0.9 wt % of Pt, 0.057-0.3 wt % of Pd, 0.03-0.1 wt % of Rh, 5.0-15.0 wt % of Ba, 10-30 wt % of CeO₂, 48.7-84.513 wt % of a composite of MgO and Al₂O₃, and 0-5 wt % of an additive based on a total weight of the APC.

The additive may include at least one of La, Zr, Mg, and Pr.

The composite of MgO and Al₂O₃ may include 15-25 wt % of MgO based on a total weight of the composite of MgO and Al₂O₃.

In other aspect, the APC may include Pt, Pd and CeO2, wherein a weight ratio of Pt to Pd is 3:1 to 7:1, and wherein weight ratio of the CeO2 to a total weight of the APC is 10-25 wt %.

In other aspect, the APC may include 0.4-0.9 wt % of Pt, 0.057-0.3 wt % of Pd, 0.03-0.1 wt % of Rh, 5.0-15.0 wt % of Ba, 10-25 wt % of CeO₂, 48.7-79.513 wt % of a composite of MgO and Al₂O₃, and 0-10 wt % of an additive based on a total weight of the APC.

The additive may include at least one of La, Zr, Mg, and Pr.

The composite of MgO and Al₂O₃ may include 15-25 wt % of MgO based on a total weight of the composite of MgO and Al₂O₃.

According to forms of the present disclosure, the amount of NH₃ supplied to the SCR catalyst at the rich air/fuel ratio can be increased by disposing the APC between the TWC and the SCR catalyst. Thus, the number and the duration where the engine operates at the rich air/fuel ratio may be reduced, thereby improving fuel economy.

CO slipped from the TWC and the APC can be purified by disposing a CO clean-up catalyst at a downstream of the SCR catalyst.

Further areas of applicability will become apparent from the description provided herein. It should be understood that the description and specific examples are intended for purposes of illustration only and are not intended to limit the scope of the present disclosure.

DRAWINGS

In order that the disclosure may be well understood, there will now be described various forms thereof, given by way of example, reference being made to the accompanying drawings, in which:

FIG. 1 is a schematic diagram of an after treatment system according to a form of the present disclosure;

FIG. 2 is a schematic diagram of an after treatment system according to another form of the present disclosure;

FIG. 3 is a schematic diagram of an after treatment system according to another form of the present disclosure;

FIG. 4 is a graph showing an amount of NH₃ accumulated over time at a downstream of an APC and an additional TWC and an amount of CO accumulated over time at a downstream of a CUC when an air/fuel ratio is rich;

FIG. 5 is a graph showing an amount of H₂ at a downstream of an APC and an additional TWC when the air/fuel ratio is rich;

FIG. 6 is a graph showing an amount of CO at a downstream of an APC and an additional TWC when the air/fuel ratio is rich;

FIG. 7 is a graph showing an amount of NH₃ produced according to the weight ratio of Pt to Pd in an APC; and

FIG. 8 is a graph showing a cumulative amount of NH₃ and an average concentration of H₂ according to an amount of CeO₂ contained in an APC.

It should be understood that the above-referenced drawings are not necessarily to scale, presenting a somewhat simplified representation of various features illustrative of the basic principles of the disclosure. The specific design features of the present disclosure, including, for example, specific dimensions, orientations, locations, and shapes, will be determined in part by the particular intended application and use environment.

The drawings described herein are for illustration purposes only and are not intended to limit the scope of the present disclosure in any way.

DETAILED DESCRIPTION

The following description is merely exemplary in nature and is not intended to limit the present disclosure, application, or uses. It should be understood that throughout the drawings, corresponding reference numerals indicate like or corresponding parts and features.

The terminology used herein is not intended to be limiting of the present disclosure. As used herein, the singular forms “a,” “an,” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises” and/or “comprising,” when used in this specification, specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof. As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items. The term “coupled” denotes a physical relationship between two components whereby the components are either directly connected to one another or indirectly connected via one or more intermediary components.

It is understood that the term “vehicle,” “vehicular,” “car,” or other similar term as used herein is inclusive of motor vehicles, in general, such as passenger automobiles including sports utility vehicles (SUV), buses, trucks, various commercial vehicles, watercraft including a variety of boats and ships, aircraft, and the like, and includes hybrid vehicles, electric vehicles, hybrid electric vehicles, hydrogen-powered vehicles and other alternative fuel vehicles (e.g., fuels derived from resources other than petroleum).

Additionally, it is understood that one or more of the below methods, or aspects thereof, may be executed by at least one controller. The term “controller” may refer to a hardware device that includes a memory and a processor. The memory is configured to store program instructions, and the processor is specifically programmed to execute the program instructions to perform one or more processes which are described further below. Moreover, it is understood that the below methods may be executed by a system comprising the controller, as described in detail below.

Furthermore, the controller of the present disclosure may be embodied as non-transitory computer readable media containing executable program instructions executed by a processor or the like. Examples of the computer readable mediums include, but are not limited to, ROM, RAM, compact disc (CD)-ROMs, magnetic tapes, floppy disks, flash drives, smart cards, and optical data storage devices. The computer readable recording medium can also be distributed throughout a computer network so that the program instructions are stored and executed in a distributed fashion, e.g., by a telematics server or a Controller Area Network (CAN).

Hereinafter, forms of the present disclosure will be described in detail with reference to the accompanying drawings.

FIG. 1 is a schematic diagram of an after treatment system according to a form of the present disclosure; FIG. 2 is a schematic diagram of an after treatment system according to another form of the present disclosure; and FIG. 3 is a schematic diagram of an after treatment system according to other form of the present disclosure.

As shown in FIG. 1, an after treatment system according to a form of the present disclosure includes an engine 10, an exhaust pipe 20, a three-way catalyst (TWC) 30, an ammonia production catalyst (APC) 40, a selective catalytic reduction (SCR) catalyst 50 and a CO clean-up catalyst (CUC) 60. As shown in FIG. 2 and FIG. 3, the after treatment system may further include a particulate filter 70.

The engine 10 burns an air/fuel mixture to convert chemical energy into mechanical energy. The engine 10 is connected to an intake manifold 16 to flow air into a combustion chamber 12. An exhaust gas generated in combustion process is collected in an exhaust manifold 18 and then flows out from the engine 10. The combustion chamber 12 is equipped with a spark plug 14 to ignite the air/fuel mixture within the combustion chamber 12. The engine 10 may be a gasoline engine. Depending on types of gasoline engines, fuel may be directly injected into the combustion chamber 12 or the air/fuel mixture may be supplied to the combustion chamber 12 via the intake manifold 16.

The exhaust pipe 20 is connected to the exhaust manifold 18 to discharge the exhaust gas to an outside of the vehicle. The exhaust pipe 20 is equipped with the TWC 30, the APC 40, the SCR catalyst 50, the CUC 60 and/or the particulate filter 70 to purify or remove emission and particulate matter contained in the exhaust gas.

The TWC 30 is disposed on the exhaust pipe 20 through which the exhaust gas discharged from the engine 10 flows, and harmful materials including CO, HC, and NOx contained in the exhaust gas are converted into harmless components by an oxidation-reaction reaction. In addition, the TWC 30 can reduce the NOx contained in the exhaust gas to NH₃ when an air/fuel ratio (AFR) is rich. Since the TWC 30 is well known to a person of an ordinary skill in the art, a detailed description thereof will be omitted.

The APC 40 is disposed on the exhaust pipe 20 at a downstream of the TWC 30. The APC 40 stores the NOx contained in the exhaust gas at a lean AFR, and generates H₂ to release the stored NOx and generates NH₃ using the released NOx and the generated H₂.

In one aspect, the APC 40 includes 0.4-0.9 wt % of Pt, 0.057-0.3 wt % of Pd, 0.03-0.1 wt % of Rh, 5.0-15.0 wt % of Ba, 10-30 wt % of CeO₂, 48.7-84.513 wt % of a composite of MgO and Al₂O₃, and 0-5 wt % of an additive based on a total weight of the APC 40.

In another aspect, the APC 40 includes 0.4-0.9 wt % of Pt, 0.057-0.3 wt % of Pd, 0.03-0.1 wt % of Rh, 5.0-15.0 wt % of Ba, 10-25 wt % of CeO₂, 48.7-79.513 wt % of the composite of MgO and Al₂O₃, and 0-10 wt % of the additive based on the total weight of the APC.

The additive is added for the performance improvement of CeO₂ and Al₂O₃ and includes at least one of La, Zr, Mg and Pr.

The Pt contained in the APC 40 functions to oxidize the NOx for the APC 40 to store the NOx. In addition, the Pt increases an amount of H₂ generated in the APC 40.

The Pd contained in the APC 40 improves heat resistance of the APC 40. Since the APC 40 is disposed close to the engine 10, a temperature of the APC 40 can rise to 950° C. Therefore, the Pd is added in the APC 40 to improve heat resistance.

In order to increase the NH₃ generation and the H₂ generation, a weight ratio of the Pt to the Pd in the APC 40 may be 3:1-7:1. In one aspect, the weight ratio of the Pt to the Pd in the APC 40 may be 3:1-5:1.

The Rh contained in the APC 40 purifies the NOx contained in the exhaust gas at a stoichiometric AFR.

The Ba and the CeO₂ contained in the APC 40 is configured to store the NOx in nitrate form.

In addition, the CeO₂ increases H₂ generation. However, if the APC 40 contains large amounts of the CeO₂, the generated NH₃ can be reoxidized. Thus, the APC 40 may include 10-30 wt % of CeO₂ based on a total weight of the APC 40.

The composite of MgO and Al₂O₃ contained in the APC 40 functions as a substrate. The composite of MgO and Al₂O₃ may include 15-25 wt % of MgO based on a total weight of the composite of MgO and Al₂O₃. The MgO enhances thermal stability of the Ba.

The SCR catalyst 50 is mounted on the exhaust pipe 20 at a downstream of the APC 40. The SCR catalyst 50 stores the NH₃ generated in the TWC 30 and the APC 40 at the rich AFR and reduces the NOx contained in the exhaust gas using the stored NH₃ at a lean AFR. This type of the SCR catalyst 50 may be referred to as a passive type SCR catalyst 50.

The SCR catalyst 50 may be composed of or include one or a combination of a zeolite catalyst and a metal catalyst supported in a porous Al₂O₃. At least one of Cu, Pt, Mn, Fe, Co, Ni, Zn, Cs and Ga may be ion-exchanged in the zeolite catalyst. In the metal catalyst supported in the porous Al₂O₃, at least one metal among Pt, Pd, Rh, Ir, Ru, W, Cr, Mn, Fe, Co, Cu, Zn and Ag may be supported in the porous Al₂O₃.

The CUC 60 is mounted on the exhaust pipe 20 at a downstream of the SCR catalyst 50. The CUC 60 purifies the CO contained in the exhaust gas. Particularly, the CO may be slipped from the TWC 30 and the APC 40 at the rich AFR. Therefore, emission of the CO to the outside of the vehicle can be prevented or inhibited by disposing the CUC 60 at the most downstream of the after treatment system. The CUC 60 includes Pt, Pd, Rh, and Ba supported in CeO₂ and Al₂O₃.

In one aspect, the CUC 60 includes 0.2-1.5 wt % of Pt, 0-0.4 wt % of Pd, 0-0.4 wt % of Rh, 0-5.0 wt % of Ba, 40-90 wt % of CeO₂, 9.8-59.8 wt % of Al₂O₃, and 0-10 wt % of an additive based on a total weight of the CUC 60.

In another aspect, the CUC 60 includes 0.2-1.5 wt % of Pt, 0-0.4 wt % of Pd, 0-0.4 wt % of Rh, 0-5.0 wt % of Ba, 40-90 wt % of CeO₂, 9.8-59.8 wt % of Al₂O₃, and 0-20 wt % of an additive based on a total weight of the CUC 60.

The additive is added for improving performance of the CeO₂ and the Al₂O₃ and includes at least one of La, Zr, Mg and Pr.

As shown in FIG. 2 and FIG. 3, the after treatment system may further include the particulate filter (GPF) 70. The particulate filter 70 may be disposed between the TWC 30 and the APC 40 (see FIG. 2) or between the APC 40 and the SCR catalyst 50 (see FIG. 3). The particulate filter 70 traps the particulate matter contained in the exhaust gas and burns the trapped particulate matter.

The exhaust pipe 20 may be equipped with a plurality of sensors for detecting the AFR of the exhaust gas and operation of the catalysts 30, 40, 50 and 60. For example, a plurality of temperature sensors 42 may be mounted at various points of the exhaust pipe 20 to detect the temperature of the exhaust gas at the various points of the exhaust pipe 20. In addition, the exhaust pipe 20 can be equipped with at least one oxygen sensor or lambda sensor at various points to detect the AFR of the exhaust gas. An intake system is equipped with an air flowmeter to detect an amount of an intake air.

The after treatment system may further include a controller. The controller is electrically connected to the sensors to receive the signals corresponding to the detected values by the sensors and determines driving condition of the vehicle, the AFR, and temperatures of the catalysts 30, 40, 50, and 60 based on the signals. The controller may control ignition timing, fuel injection timing, fuel amount, etc. based on the determination results.

EXAMPLES

Hereinafter, performance of the APC 40 will be described through various examples and comparative examples. The compositions of various examples and comparative examples are shown in [Table 1].

TABLE 1 MgO- additive Pt(wt %) Pd(wt %) Rh(wt %) BaO(wt %) CeO₂(wt %) Al₂O₃ (wt %) (wt %) Comparative Applying additional TWC instead of APC Example 1 Comparative Pt + Pd = 0.8 0.05 10 20 69.15 1.4 Example 2 (Pt:Pd = 2:1) Example 1 Pt + Pd = 0.8 0.05 10 20 69.15 1.4 (Pt:Pd = 3:1) Example 2 Pt + Pd = 0.8 0.05 10 20 69.15 1.4 (Pt:Pd = 4:1) Example 3 Pt + Pd = 0.8 0.05 10 20 69.15 1.4 (Pt:Pd = 5:1) Example 4 Pt + Pd = 0.8 0.05 10 20 69.15 1.4 (Pt:Pd = 7:1) Comparative Pt + Pd = 0.8 0.05 10 20 69.15 1.4 Example 3 (Pt:Pd = 9:1) Comparative Pt + Pd = 0.8 0.05 10 0 89.15 1.4 Example 4 (Pt:Pd = 4:1) Example 5 Pt + Pd = 0.8 0.05 10 10 79.25 1.3 (Pt:Pd = 4:1) Example 6 Pt + Pd = 0.8 0.05 10 30 59.45 1.1 (Pt:Pd = 4:1) Comparative Pt + Pd = 0.8 0.05 10 40 49.55 1.0 Example 5 (Pt:Pd = 4:1) Comparative Pt + Pd = 0.8 0.05 10 50 39.65 0.9 Example 6 (Pt:Pd = 4:1)

(Test 1: Performance Comparison Between APC and Additional TWC)

For test 1, the TWC 30, the GPF 70, the SCR catalyst 50 and the CUC 60 are sequentially disposed on the exhaust pipe 20. In Comparative Example 1 the additional TWC is disposed between the GPF 70 and the SCR catalyst 50, and in Example 2 the APC 40 is disposed between the GPF 70 and the SCR catalyst 50. After that, 2.0 L, 4-cylinders, lean-burn gasoline engine is connected to the exhaust pipe 20 and aging treatment is performed. The aging treatment is carried out for 50 hours at 1,000° C. on the TWC 30 basis.

The lean AFR (A=1.8) is maintained for 5 minutes at an engine speed of 2,000 rpm to cause the entire after treatment system to be lean atmosphere. Thereafter, an amount of NH₃ accumulated at the downstream of the APC 40 and the additional TWC over time, and an amount of CO accumulated at the downstream of the CUC 60 over time are measured while the rich AFR (λ=0.97) is maintained at the engine speed of 2,000 rpm.

FIG. 4 is a graph showing an amount of NH₃ accumulated over time at a downstream of an APC and an additional TWC and an amount of CO accumulated over time at a downstream of a CUC when an air/fuel ratio is rich.

In FIG. 4, a thick solid line represents the amount of NH₃ accumulated at the downstream of the APC 40 in Example 2 and a thin solid line represents the amount of NH₃ accumulated at the downstream of the additional TWC in Comparative Example 1. Also, a thick dotted line represents the amount of CO accumulated at the downstream of the CUC 60 in Example 2 and a thin dotted line represents the amount of CO accumulated at the downstream of the CUC 60 in Comparative Example 1.

As shown in FIG. 4, since the APC 40 has more oxygen storage material (ie, CeO₂) than the additional TWC, a delay time from beginning of the rich AFR to beginning of NH₃ generation increases slightly (about 2-3 seconds). However, the APC 40 generates a large amount of NH₃ when the AFR is rich, using the stored NOx at the lean AFR. Therefore, the amount of the NH₃ accumulated at the downstream of the APC 40 becomes greater than the amount of the NH₃ accumulated at the downstream of the additional TWC with the lapse of time. Resultantly, the APC 40 increases the amount of the NH₃ generation and supplies more NH₃ to the SCR catalyst 50 disposed at the downstream of the APC 40.

Also, a time at which the CO begins to slip from the CUC 60 in a case of Example 2 is slower than the time at which the CO begins to slip from the CUC 60 in a case of Comparative Example 1 (by about 5 seconds).

On the other hand, by modifying Test 1, the lean AFR and the rich AFR are repeated at regular intervals, and amounts of the H₂ and the CO are measured at the downstream of the APC 40 and the additional TWC.

FIG. 5 is a graph showing an amount of H₂ at a downstream of an APC and an additional TWC when the air/fuel ratio is rich, and FIG. 6 is a graph showing an amount of CO at a downstream of an APC and an additional TWC when the air/fuel ratio is rich.

In FIG. 5, a thick solid line represents the amount of H₂ at the downstream of the APC 40 at the rich AFR and a thin solid line represents the amount of H₂ at the downstream of the additional TWC at the rich AFR. In FIG. 6, a thick solid line represents the amount of CO at the downstream of the APC 40 at the rich AFR and a thin solid line represents the amount of CO at the downstream of the additional TWC at the rich AFR.

As shown in FIGS. 5 and 6, the amount of H₂ at the downstream of the APC 40 is greater than the amount of H₂ at the downstream of the additional TWC at the rich AFR, whereas the amount of CO at the downstream of the APC 40 is smaller than the amount of CO at the downstream of the additional TWC. Resultantly, the APC 40, compared to the additional TWC, supplies more H₂ to the CUC 60 while supplying less CO to the CUC 60.

(Test 2: Performance Comparison According to Compositions in APC)

For test 2, the TWC 30 and the APC 40 are sequentially disposed on the exhaust pipe 20. After that, 2.0 L, 4-cylinders, lean-burn gasoline engine is connected to the exhaust pipe 20 for aging treatment. The aging treatment is carried out for 50 hours at 1000° C. on the TWC 30 basis and for 50 hours at 930° C. on the APC 40 basis.

The aged TWC 30 and the aged APC 40 are respectively cut to 1-inch diameter and 1-inch length to create a TWC sample and an APC sample, and the TWC sample and the APC sample are connected to a lean-rich gas supply device. The lean-rich gas supply device is a device that supplies gas with a composition similar to the exhaust gas composition of the lean-burn engine.

After the lean AFR (λ=1.8) is maintained for 5 minutes, the AFR is changed to be rich (λ=0.97) using the lean-rich gas supply device. The amount of NH₃ for 20 seconds at the rich AFR (λ=0.97) is measured. At this time, the temperature of the TWC 30 is adjusted to 500° C. and the temperature of the APC 40 is adjusted to 450° C.

FIG. 7 is a graph showing an amount of NH₃ produced according to the weight ratio of Pt to Pd in an APC.

As shown in Table 1, the weight ratios of the Rh, the BaO, the CeO₂, the composite of MgO and Al₂O₃, and the additive are the same in Comparative Example 2, Example 1, Example 2, Example 3, Example 4 and Comparative Example 3. The total weight ratios of the Pt and the Pd are the same but the weight ratios of the Pt to the Pd are different in Comparative Example 2, Example 1, Example 2, Example 3, Example 4 and Comparative Example 3.

As shown in FIG. 7, the NH₃ production in the APC 40 is the greatest in Example 2, and the NH₃ production in the APC 40 is appropriate in Example 1 to Example 4. However, the NH₃ production in the APC 40 is small in Comparative Example 2 and Comparative Example 3. As described above, to increase NH₃ production by increasing H₂ production, the content of the Pt may be increased but the Pd may function to improve heat resistance and thermal durability. Particularly, if the APC 40 contains a small amount of the Pd (e.g., in Comparative Example 2), it can be seen that the APC 40 is exposed to high temperature and the ability to generate NH₃ is reduced. In contrast, if the APC 40 contains a large amount of the Pd (e.g., in Comparative Example 3), the amount of the Pt contained in the APC 40 is reduced and the NH₃ production is also reduced. Therefore, the ratio of the Pt to the Pd in the APC 40 may be 3:1-7:1 in one aspect. In one form, the ratio of the Pt to the Pd in the APC 40 may be 3:1 to 5:1.

FIG. 8 is a graph showing a cumulative amount of NH₃ and an average concentration of H₂ according to an amount of CeO₂ contained in an APC.

As shown in Table 1, the total weight ratios of the Pt and the Pd, the weight ratios of the Pt to the Pd, and the weight ratios of the BaO are the same in Comparative Example 4, Example 5, Example 2, Example 6, Comparative Example 5. The weight ratios of CeO₂ are changed and the weight ratios of the composite of MgO and Al₂O₃ are changed accordingly in Comparative Example 4, Example 5, Example 2, Example 6, Comparative Example 5, and Comparative Example 6. The weight ratios of the additive vary in Comparative Example 4, Example 5, Example 2, Example 6, Comparative Example 5, and Comparative Example 6, but do not significantly affect the performance of the APC 40. In addition, the amount of the CeO₂ contained in the APC 40 is gradually increased in Comparative Example 4, Example 5, Example 2, Example 6, Comparative Example 5, and Comparative Example 6.

As shown in FIG. 8, the amount of the NH₃ produced in the APC 40 is the greatest in Example 2, and the concentration of the H₂ produced in the APC 40 is also considerably high. As the amount of the CeO₂ increases, the concentration of the H₂ also increases in Comparative Example 4, Example 5, Example 2, Example 6, Comparative Example 5, and Comparative Example 6. However, if the amount of the CeO₂ exceeds 20 wt % based on the total weight of the APC 40, a ratio of H₂ concentration increase to CeO₂ increase is slowed down. In addition, if the amount of the CeO₂ exceeds 30 wt % based on the total weight of the APC 40 (in Comparative Example 5 and Comparative Example 6), the concentration of the generated H₂ is high, but the NH₃ generation sharply decreases due to increase of O₂ stored in the APC 40. In this case, the produced NH₃ is reoxidized by the O₂ stored in the APC 40. Therefore, it may be desirable that the amount of CeO₂ is 10-30 wt % based on the total weight of the APC 40 in order to improve the NH₃ production ability of the APC 40. In one form, the amount of CeO₂ to the total weight of the APC 40 may be 10-25 wt %.

It is to be understood that the disclosure is not limited, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the disclosure. 

1. An ammonia production catalyst (APC) comprising 0.4-0.9 wt % of Pt, 0.057-0.3 wt % of Pd, 0.03-0.1 wt % of Rh, 5.0-15.0 wt % of Ba, 10-30 wt % of CeO₂, 48.7-84.513 wt % of a composite of MgO and Al₂O₃, and 0-5 wt % of an additive based on a total weight of the APC.
 2. The APC of claim 1, wherein the additive comprises at least one of La, Zr, Mg, and Pr.
 3. The APC of claim 1, wherein the composite of MgO and Al₂O₃ includes 15-25 wt % of MgO based on a total weight of the composite of MgO and Al₂O₃.
 4. The APC of claim 1, wherein a weight ratio of Pt to Pd is 3:1 to 7:1.
 5. An ammonia production catalyst (APC) comprising 0.4-0.9 wt % of Pt, 0.057-0.3 wt % of Pd, 0.03-0.1 wt % of Rh, 5.0-15.0 wt % of Ba, 10-25 wt % of CeO₂, 48.7-79.513 wt % of a composite of MgO and Al₂O₃, and 0-10 wt % of an additive based on a total weight of the APC
 6. The APC of claim 5, wherein the additive comprises at least one of La, Zr, Mg, and Pr.
 7. The APC of claim 5, wherein the composite of MgO and Al₂O₃ includes 15-25 wt % of MgO based on a total weight of the composite of MgO and Al₂O₃.
 8. The APC of claim 5, wherein a weight ratio of Pt to Pd is 3:1 to 7:1.
 9. An after treatment system comprising: an exhaust pipe through which an exhaust gas flows; a three-way catalyst (TWC) mounted on the exhaust pipe and purifying HC, CO, and NOx contained in the exhaust gas; an ammonia production catalyst (APC) mounted on the exhaust pipe at a downstream of the TWC, storing NOx at a lean air/fuel ratio, and generating H₂, releasing the stored NOx, and generating NH₃ using the released NOx and the generated H₂ at a rich air/fuel ratio; and a selective catalytic reduction (SCR) catalyst mounted on the exhaust pipe at a downstream of the APC, storing the NH₃ generated in the TWC and the APC, and reducing the NOx contained in the exhaust gas using the stored NH₃. he fastening apparatus of claim 8, wherein the bevel ring gear is fixed to the at least one support plate.
 10. The after treatment system of claim 9, further comprising a CO clean-up catalyst (CUC) mounted on the exhaust pipe at a downstream of the SCR catalyst and purifying the CO contained in the exhaust gas.
 11. The after treatment system of claim 10, further comprising a particulate filter disposed between the TWC and the APC or between the APC and the SCR catalyst, wherein the particulate filter traps particulate matter in the exhaust gas.
 12. The after treatment system of claim 9, wherein the APC comprises Pt, Pd and CeO₂, wherein a weight ratio of Pt to Pd is 3:1 to 7:1, and wherein weight ratio of the CeO₂ to a total weight of the APC is 10-30 wt %.
 13. The after treatment system of claim 9, wherein the APC comprises 0.4-0.9 wt % of Pt, 0.057-0.3 wt % of Pd, 0.03-0.1 wt % of Rh, 5.0-15.0 wt % of Ba, 10-30 wt % of CeO₂, 48.7-84.513 wt % of a composite of MgO and Al₂O₃, and 0-5 wt % of an additive based on a total weight of the APC.
 14. The after treatment system of claim 13, wherein the additive comprises at least one of La, Zr, Mg, and Pr.
 15. The after treatment system of claim 13, the composite of MgO and Al₂O₃ includes 15-25 wt % of MgO based on a total weight of the composite of MgO and Al₂O₃.
 16. The after treatment system of claim 9, wherein the APC comprises Pt, Pd and CeO₂, wherein a weight ratio of Pt to Pd is 3:1 to 7:1, and wherein weight ratio of the CeO₂ to a total weight of the APC is 10-25 wt %.
 17. The after treatment system of claim 9, wherein the APC comprises 0.4-0.9 wt % of Pt, 0.057-0.3 wt % of Pd, 0.03-0.1 wt % of Rh, 5.0-15.0 wt % of Ba, 10-25 wt % of CeO₂, 48.7-79.513 wt % of a composite of MgO and Al₂O₃, and 0-10 wt % of an additive based on a total weight of the APC.
 18. The after treatment system of claim 17, wherein the additive comprises at least one of La, Zr, Mg, and Pr.
 19. The after treatment system of claim 17, the composite of MgO and Al2O3 includes 15-25 wt % of MgO based on a total weight of the composite of MgO and Al2O3. 